Bitumen Based Coating Enamel Grade C
Bitumen Based Coating Enamel Grade C  Bitumen Based Coating Enamel Grade C  Johor Bahru JB Malaysia Supply Suppliers Manufacturers | Cascadian Asphalt Industries Sdn Bhd
Bitumen Based Coating Enamel Grade C

Price: RM 1650/-(EX-FACTORY in Paper Bags. Valid until 30/09/2015)
  




Bitumen Based Coating Enamel is a bituminous compound reinforced with inert non-fibrous fillers for hot application. Type 2 a, b and c comply with BS 4147: 1980. It will soften gradually when heated and will change back to solid on cooling.


USAGE
Bitumen Based Coating Enamel is mainly used as anti-corrosion materials for protection of iron and steel pipes for industrial and drinking water.


TECHNICAL ADVANTAGES
  • Excellent and permanent adhesion to metal

  • Low water absorption

  • Impact resistance

  • Flexibility

  • Resistance to soil stress

  • Resistance to cold stress

  • High electrical resistibility

  • Chemically stable


    SPECIFICATIONS

    Characterisitics
    Grade C
    Test Methods
    Filler content by ignition , % by mass
    45 to 55
    Appendix B
    Density at 25°C, g/cm³
    1.4 to 1.65
    Appendix C
    Softening point (Ring and Ball ), °C
    120 to 150
    BS 2000:Part 58
    Penetration at 25°C, 10-1 mm
    5 to 15
    Appendix D
    Flash point (Cleveland Open Cup), min., °C
    260
    BS 4689

    Sag, max.,mm
        60°C, 24 h
        75°C, 24 h


    -
    1.5
    Appendix E
     
     
    Bend at 0°C, min., mm
    10
    Appendix F

    Impact Disbonded area, min., mm²
        0°C
        25°C


    -
    6500
    Appendix G

     
    Peel, initial and delayed, max., mm
        30°C
        40°C
        50°C
        60°C
       
    -
    3.0
    3.0
    3.0
    Appendix H



     



    APPLICATION AND HANDLING

  • Surface Preparation
         The surface of the steel pipe to be coated with Bitumen Based Coating Enamel shall
         be wire-brushed to remove all surface rust, mill scale and loose materials. Immediately
         after wire brushing the surface shall be wiped clean and dried, then apply a coat of
         Bituminous Primer and allowed to dry.


  • Application
         Bitumen Based Coating Enamel shall be broken up into small pieces and heated
         slowly to the application temperature of 220°C to 250°C, and should not be heated
         to a temperature exceeding 270°C.



    DRUMMING OPTIONS
    (Grade A+) Brand New Drum

    (Grade A) Recondition Drums . 
    External painted in Black   
    Internal washed and 100% cleaned

    (Grade B) Recondition Drums .
    External painted in Black
    Internal containing 2 to 3 Kg
    Foreign material .

    (Grade C) Recondition Drums .
    External unpainted .
    Internal containing 2 to 3 Kg Foreign material .


    PAPER PACKING
    2 PLY PAPER BAG+1 PLY POLY BAG = 3 PLY PAPER BAGS IN NET WEIGHT 50/25 KGS BAGS